包胶TPE，TPE 49D

 

Telcar® TELC-1000-92

热塑性弹性体

 

Teknor Apex公司

 

Technical Data

 

产品说明

Telcar TELC 1000-92 is a high hardness, low density general purpose thermoplastic elastomer designed for interior injection molding applications in the automotive industry.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Processing (English)

•  Technical Datasheet

搜索 UL 黄卡 •  Teknor Apex公司

•  Telcar®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

特性 • Low Specific Gravity • 流动性低 • 硬度高

• 低密度 • 填充

用途 • 汽车内部零件

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 额定值(英制) 额定值(公制) 测试方法

比重 0.913 0.911g/cm³ ASTM D792

熔流率（熔体流动速率） (230°C/2.16 kg) 2.6g/10 min 2.6g/10 min ASTM D1238

收缩率 - 流动 ASTM D955

356°F (180°C), 30分钟 0.013in/in 1.3%

24小时 0.011in/in 1.1%

机械性能 额定值(英制) 额定值(公制) 测试方法

弯曲模量 42100psi 290MPa ASTM D790

弹性体 额定值(英制) 额定值(公制) 测试方法

拉伸应力 ASTM D412

流量 : 100%应变 1390psi 9.60MPa

横向流量 : 100%应变 3 1020psi 7.02MPa

抗张强度 ASTM D412

流量 : 屈服 1440psi 9.90MPa

横向流量 : 屈服 3 1070psi 7.40MPa

伸长率 ASTM D412

横向流量 : 断裂 3 370% 370%

流量 : 断裂 4 270% 270%

撕裂强度 - 横向流量 497lbf/in 87.0kN/m ASTM D624

压缩永久变形 ASTM D395

73°F (23°C), 22 hr 60% 60%

158°F (70°C), 22 hr 74% 74%

194°F (90°C), 70 hr 93% 93%

冲击性能 额定值(英制) 额定值(公制) 测试方法

悬壁梁缺口冲击强度 (-40°F (-40°C)) 无断裂 无断裂 ASTM D256

落锤冲击 (-22°F (-30°C)) 300in·lb 33.9J ASTM D3029

拉伸冲击强度 224ft·lb/in² 471kJ/m² ASTM D1822

硬度 额定值(英制) 额定值(公制) 测试方法

肖氏硬度 ASTM D2240

邵氏 D, 1 秒 49 49

邵氏 D, 5 秒 41 41

 

Telcar® TELC-1000-92

热塑性弹性体

Teknor Apex公司

热性能 额定值(英制) 额定值(公制) 测试方法

载荷下热变形温度 ASTM D648

66 psi (0.45 MPa), 未退火 145°F 62.5°C

264 psi (1.8 MPa), 未退火 105°F 40.7°C

玻璃转化温度 -68.6°F -55.9°C DSC

线形热膨胀系数 ASTM D696

流动 : -22 到 86°F (-30 到 30°C) 6.6E-5in/in/°F 1.2E-4cm/cm/°C

横向 : -22 到 86°F (-30 到 30°C) 6.5E-5in/in/°F 1.2E-4cm/cm/°C

老化 额定值(英制) 额定值(公制) 测试方法

空气中拉伸强度的变化率 ASTM D573

230°F (110°C), 1008 hr 1.6% 1.6%

257°F (125°C), 168 hr 4.3% 4.3%

空气中极限伸长率的变化率 ASTM D573

230°F (110°C), 1008 hr -43% -43%

257°F (125°C), 168 hr -40% -40%

空气中硬度计硬度的变化率 (支撐 D, 230°F 1.7 1.7 ASTM D573

(110°C), 1008 hr)

可燃性 额定值(英制) 额定值(公制) 测试方法

燃烧速率 1.2in/min 30mm/min ISO 3795

充模分析 额定值(英制) 额定值(公制) 测试方法

表观粘度 (392°F (200°C), 206 sec^-1) 516Pa·s 516Pa·s ASTM D3835

补充信息

Instrumented Dart Impact Energy @ Yield, -40°C, 9000 in/min, Ductile Failure: 200 in-lbs Instrumented Dart Impact Deflection @ Break, -40°C, 9000 in/min, Ductile Failure: 1359 mils Instrumented Dart Impact Energy @ Break, -40°C, 9000 in/min, Ductile Failure: 350 in-lbs Fogging, Kaake Buchler, 3 hrs, 100°C: 92

Tear Strength, ASTM D1004, Die C: 364 lb/in

Heat Aging Performance Izod Impact, 1000 hrs, 120°C: No Break Flammability Burn Rate, FMVSS 302, Max 100, 30.2 mm/min: Pass Flammability Burn Rate, FMVSS 302, Max 100, 1.2 in/min: Pass

Poisson's Ratio, ASTM D 638, @-35°C = 0.337, @+23°C = 0.419, @+85°C = 0.363

 

法律声明

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

 

注射 额定值(英制) 额定值(公制)

料筒后部温度 340 到 380°F 171 到 193°C

料筒中部温度 350 到 390°F 177 到 199°C

料筒前部温度 360 到 400°F 182 到 204°C

射嘴温度 370 到 410°F 188 到 210°C

加工（熔体）温度 370 到 410°F 188 到 210°C

模具温度 77.0 到 150°F 25.0 到 65.6°C

注塑压力 200 到 1000psi 1.38 到 6.89MPa

注射速度 中等偏快 中等偏快

背压 25.0 到 50.0psi 0.172 到 0.345MPa

螺杆转速 50 到 100rpm 50 到 100rpm

垫层 0.150 到 1.00in 3.81 到 25.4mm

挤出 额定值(英制) 额定值(公制)

干燥温度 176°F 80.0°C

干燥时间 2.0hr 2.0hr

料筒1区温度 330 到 370°F 166 到 188°C

 

Telcar® TELC-1000-92

热塑性弹性体

Teknor Apex公司

挤出 额定值(英制) 额定值(公制)

料筒2区温度 340 到 380°F 171 到 193°C

料筒3区温度 350 到 390°F 177 到 199°C

料筒5区温度 360 到 400°F 182 到 204°C

口模温度 374 到 410°F 190 到 210°C

挤压说明

螺杆转速30 - 100 rpm

 

 

 

 

TPE Telcar® TELC-1000-92,热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生